CHAPTER 2 > MATERIALS > TABLES > TABLE 3 | | |
| | |
| Molar entropy of fusion and vaporization | | |
| Mo / kg/mole | T_f / K | lambda_Sf / J/(K·mole) | T_v / K | lambda_Sv / J/(K·mole) | Aluminum | 0.027 | 887 | 12.1 | 2720 | 108 | Copper | 0.064 | 1356 | 9.68 | 2860 | 107 | Gallium | 0.070 | 303 | 18.7 | 2500 | 102 | Gold | 0.197 | 1336 | 9.69 | 2950 | 110 | Iron | 0.056 | 1808 | 8.58 | 3000 | 118 | Lead | 0.207 | 600 | 7.94 | 2020 | 880 | Mercury | 0.201 | 234 | 10.1 | 630 | 91 | Platinum | 0.195 | 2042 | 10.6 | 4270 | 105 | Silicon | 0.028 | 1693 | 2.17 | 2900 | 136 | Sodium | 0.023 | 371 | 7.01 | | | Tungsten | 0.184 | 3653 | 9.67 | 5770 | 139 | Water | 0.018 | 273 | 22.0 | 373 | 109 | | | | | | | | | | lambda_Sf / J/(K·kg) | | | Granite | | 1170 | 360 | | | | |
| T_f: Temperature of fusion/melting T_v: Temperature of vaporization/condensation Mo: Molar mass | | |
| | | | | | |